Modified ZIF-8 mixed matrix membrane for CO2/CH4 separation

Tunability of metal-organic frameworks (MOFs) properties enables them to be tailored for specific applications. In this study, zeolitic imidazole framework 8 (ZIF-8), sub-class of MOF, underwent pre-synthesis and post-synthesis modifications. The pre-synthesis modification using GO (ZIF-8/GO) shows...

Full description

Main Authors: Nordin, N.A.H.M., Ismail, A.F., Misdan, N., Nazri, N.A.M.
Format: Article
Institution: Universiti Teknologi Petronas
Record Id / ISBN-0: utp-eprints.20017 /
Published: American Institute of Physics Inc. 2017
Online Access: https://www.scopus.com/inward/record.uri?eid=2-s2.0-85031283191&doi=10.1063%2f1.5005424&partnerID=40&md5=13dea58c3578dc2eac7d7d8ac8f15260
http://eprints.utp.edu.my/20017/
Tags: Add Tag
No Tags, Be the first to tag this record!
Summary: Tunability of metal-organic frameworks (MOFs) properties enables them to be tailored for specific applications. In this study, zeolitic imidazole framework 8 (ZIF-8), sub-class of MOF, underwent pre-synthesis and post-synthesis modifications. The pre-synthesis modification using GO (ZIF-8/GO) shows slight decrease in textural properties, while the post-synthesis modification using amine solution (ZIF-8/NH2) resulted in superior BET surface area and pore volume. Mixed matrix membranes (MMMs) derived from polysulfone (PSf) and the modified ZIF-8s were then prepared via dry/wet phase inversion. The polymer chain flexibility of the resulted MMMs shows rigidification, where ZIF-8/NH2 as filler resulting higher rigidification compared to ZIF-8/GO. The MMMs were further subjected to pure CO2 and CH4 gas permeation experiments. The PSf/ZIF-8/NH2 shows superior CO2/CH4 selectivity (88 increased) while sacrificing CO2 permeance due to combination of severe polymer chain rigidification and the presence of CO2-philic group, amine. Whereas, the PSf/ZIF-8/GO possess 64 increase in CO2 permeance without notable changes in CO2/CH4 selectivity. © 2017 Author(s).

Similar Items