Structural and magnetic properties of Ni0.5Zn0.5Fe2O4 synthesized through the sol-gel method
This study investigates the influence of calcination temperatures on the magnetic properties of Ni0.5Zn0.5Fe2O4(Ni-Zn) ferrites.Ni-Zn ferrite with the chemical formula Ni0.5Zn0.5Fe2O4 was prepared from their respective nitrate salts through the sol-gel method. The resulting ferrites were characteriz...
| Main Authors: | Guan, B.H., Zahari, M.H., Chuan, L.K. |
|---|---|
| Format: | Article |
| Institution: | Universiti Teknologi Petronas |
| Record Id / ISBN-0: | utp-eprints.31832 / |
| Published: |
Trans Tech Publications Ltd
2014
|
| Online Access: |
https://www.scopus.com/inward/record.uri?eid=2-s2.0-84921631526&doi=10.4028%2fwww.scientific.net%2fAMM.664.75&partnerID=40&md5=2b29bc097dea1f009ccba272c35afa98 http://eprints.utp.edu.my/31832/ |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: |
This study investigates the influence of calcination temperatures on the magnetic properties of Ni0.5Zn0.5Fe2O4(Ni-Zn) ferrites.Ni-Zn ferrite with the chemical formula Ni0.5Zn0.5Fe2O4 was prepared from their respective nitrate salts through the sol-gel method. The resulting ferrites were characterized using X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and vibrating sample magnetometer (VSM). Single phased Ni0.5Zn0.5Fe2O4 was obtained at all calcination temperatures.FESEM Micrographs reveals an increase in the grain size with the increase of the calcination temperature. Consequently, the magnetic saturation of the samples were found to increase with each increase in the calcinations temperature where the highest value obtained is 70.58 emu/g for the samples calcined at 1000°C. © (2014) Trans Tech Publications, Switzerland. |
|---|