Chloride Induced Stress Corrosion Cracking For Thermally Insulated Austenitic Stainless Steel Type 304 Using Wick Test

Stress corrosion cracking (SCC) is a failure mechanism that takes place under residual stress conditions for various alloy/material and environmental combinations.

Main Author: RAVI, RUBEN
Format: Final Year Project
Language: English
Institution: Universiti Teknologi Petronas
Record Id / ISBN-0: utp-utpedia.20588 /
Published: IRC 2021
Subjects:
TJ Mechanical engineering and machinery
Online Access: http://utpedia.utp.edu.my/20588/1/11_UTP21-2_ME11.pdf
http://utpedia.utp.edu.my/20588/
Tags: Add Tag
No Tags, Be the first to tag this record!
id utp-utpedia.20588
recordtype eprints
spelling utp-utpedia.205882021-08-30T21:21:03Z http://utpedia.utp.edu.my/20588/ Chloride Induced Stress Corrosion Cracking For Thermally Insulated Austenitic Stainless Steel Type 304 Using Wick Test RAVI, RUBEN TJ Mechanical engineering and machinery Stress corrosion cracking (SCC) is a failure mechanism that takes place under residual stress conditions for various alloy/material and environmental combinations. IRC 2021-01 Final Year Project NonPeerReviewed application/pdf en http://utpedia.utp.edu.my/20588/1/11_UTP21-2_ME11.pdf RAVI, RUBEN (2021) Chloride Induced Stress Corrosion Cracking For Thermally Insulated Austenitic Stainless Steel Type 304 Using Wick Test. IRC, Universiti Teknologi PETRONAS. (Submitted)
institution Universiti Teknologi Petronas
collection UTPedia
language English
topic TJ Mechanical engineering and machinery
spellingShingle TJ Mechanical engineering and machinery
RAVI, RUBEN
Chloride Induced Stress Corrosion Cracking For Thermally Insulated Austenitic Stainless Steel Type 304 Using Wick Test
description Stress corrosion cracking (SCC) is a failure mechanism that takes place under residual stress conditions for various alloy/material and environmental combinations.
format Final Year Project
author RAVI, RUBEN
author_sort RAVI, RUBEN
title Chloride Induced Stress Corrosion Cracking For Thermally Insulated Austenitic Stainless Steel Type 304 Using Wick Test
title_short Chloride Induced Stress Corrosion Cracking For Thermally Insulated Austenitic Stainless Steel Type 304 Using Wick Test
title_full Chloride Induced Stress Corrosion Cracking For Thermally Insulated Austenitic Stainless Steel Type 304 Using Wick Test
title_fullStr Chloride Induced Stress Corrosion Cracking For Thermally Insulated Austenitic Stainless Steel Type 304 Using Wick Test
title_full_unstemmed Chloride Induced Stress Corrosion Cracking For Thermally Insulated Austenitic Stainless Steel Type 304 Using Wick Test
title_sort chloride induced stress corrosion cracking for thermally insulated austenitic stainless steel type 304 using wick test
publisher IRC
publishDate 2021
url http://utpedia.utp.edu.my/20588/1/11_UTP21-2_ME11.pdf
http://utpedia.utp.edu.my/20588/
_version_ 1741195640842485760
score 11.62408

Similar Items